Home | About Valvias | Login sponsor | Sponsor Info | Valvias Tv | Contact | Site Map |
Valvias The most visited portal for Valves & Actuators
  Open to all manufacturers and distributors
[+info]  
Home contact
General
Basic Concepts
Types of valves
Types of actuators
Norms & Testing
Technical Literature
Software
Search
Valve
Actuator
Company
Company on the map
Updates
Requests for Quotation
Stocks
Articles
News
Trade Fairs
Courses
Job Offers
Tools
Miscellanea
Glossary
Links
Valvias Tv
Login sponsor
Sponsor Info
About Valvias
Contact
Site Map
Basic Concepts > Design > Materials EspaƱol
 
Metals
Forged Carbon Steel
Stainless Steel
Structural Steel
Alloy Cast Steel
Carbon Cast Steel
Ductil Cast Iron
Grey Cast Iron
Other
Rubber (elastomers)
 
Google
Coefficients Cv Kv
Flow equations
Flanges
ANSI/ASME vs ISO
Valve books
Carbon Cast Steels
ASTMENDINW n°Re
(MPa)
A-216 WCA
A-216 WCBEN 10213-2 GP240GHGS C-251.0619240
EN 10213-2 GS20Mn5GS-20Mn5V 1.6220300
A-216 WCCDIN 1681 GS45-
Carbon Cast Steels stantands for valves

ASTM A216 / A216M - 08
Standard Specification for Steel Castings, Carbon, Suitable for Fusion Welding, for High-Temperature Service

This specification covers carbon steel castings for valves, flanges, fittings, or other pressure-containing parts for high-temperature service and of quality suitable for assembly with other castings or wrought-steel parts by fusion welding. Covered here are three grades of carbon steel (Grades WCA, WCB, and WCC), the selection of which shall depend on the design and service conditions, mechanical properties, and the high temperature characteristics. Castings shall be heat treated and furnished, as appropriate to their design and chemical composition, in the annealed, or normalized, or normalized and tempered conditions after they have been allowed to cool below the transformation range. Furnace temperatures for heat treating shall be effectively controlled by pyrometer. Steel castings shall adhere to chemical composition and tensile property requirements, which include tensile strength, yield strength, elongation, and reduction of area. The surface of castings shall be free of adhering elements such as sand, cracks, hot tears, and other discontinuities, and as such be repair welded when judged appropriate.